Methods and apparatus for three dimensional NAND structure fabrication

ABSTRACT

Methods and apparatus for forming a plurality of nonvolatile memory cells are provided herein. In some embodiments, the method, for example, includes forming a plurality of nonvolatile memory cells, comprising forming, on a substrate, a stack of alternating layers of metal including a first layer of metal and a second layer of metal different from the first layer of metal; removing the first layer of metal to form spaces between the alternating layers of the second layer of metal; and one of depositing a first layer of material to partially fill the spaces to leave air gaps therein or depositing a second layer of material to fill the spaces.

CROSS-REFERENCE TO RELATED APPLICATION(S)

The present application is a continuation application of U.S. patentapplication Ser. No. 16/517,956, which was filed on Jul. 22, 2019, whichclaims priority to and the benefit of U.S. Provisional PatentApplication Ser. No. 62/851,699, which was filed on May 23, 2019, theentire contents of each of these applications is incorporated herein byreference.

FIELD

Embodiments of the present disclosure generally relate to substrateprocessing equipment and techniques, and more particularly, to methodsand apparatus for three dimensional (3D) NAND structure fabrication.

BACKGROUND

To address challenges encountered in scaling planar (2D) NAND memorydevices to achieve higher densities at a lower cost per bit, ultra-highdensity, three-dimensional (3D) stacked memory structures have beenintroduced. Such 3D memory structures are sometimes referred to ashaving a Bit Cost Scalable (BiCS) architecture, and include strings ofvertically aligned memory cells. Typically, the vertically alignedmemory cells are formed from an array of alternating conductor andinsulator layers, where the conductive layers correspond to the wordlines of the memory structure.

As the number of vertically stacked memory cells in 3D NAND devicesincreases (e.g., as chip densities increase), the aspect ratio of memorycell strings also increases, introducing numerous manufacturing issues.The inventors have observed for example, that as stacking increases, thedifficulty in etching/filling and stress control also increases. Theinventors have further observed that thinning down the layers in thestack to maintain the aspect ratio of the memory cell strings withinmanageable limits results in more challenging downstream etch processes.

Accordingly, the inventor has provided methods and apparatus for 3D NANDstructure fabrication.

SUMMARY

Methods and apparatus for forming a plurality of nonvolatile memorycells are provided herein. In some embodiments, the method includesforming, on a substrate, a stack of alternating layers of metalincluding a first layer of metal and a second layer of metal differentfrom the first layer of metal; removing the first layer of metal to formspaces between the alternating layers of the second layer of metal; andone of depositing a first layer of material to partially fill the spacesto leave air gaps therein or depositing a second layer of material tofill the spaces.

In accordance with some embodiments of the present disclosure, there isprovided a semiconductor memory device that includes a substrateincluding a stack of alternating layers of material including a firstlayer of material that is at least one of metal, metal nitride, orconductive metal compound and a second layer of material that is atleast one of metal, metal alloy, or metal with dopant including one ormore metal elements, wherein the first layer of material is differentfrom the second layer of material.

In accordance with an aspect of the present disclosure, there isprovided a system for forming a plurality of nonvolatile memory cells.The system includes an apparatus configured to deposit on a substrate alayer of silicon nitride (SiN) and poly-silicon (poly-Si) and a stack ofalternating layers of metal including a first layer of metal and asecond layer of metal different from the first layer of metal; anapparatus configured to remove the first layer of metal to form spacesbetween the alternating layers of the second layer of metal; and anapparatus configured to one of deposit a first layer of material topartially fill the spaces to leave air gaps therein or deposit a secondlayer of material to fill the spaces.

Other and further embodiments of the present disclosure are describedbelow.

BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of the present disclosure, briefly summarized above anddiscussed in greater detail below, can be understood by reference to theillustrative embodiments of the disclosure depicted in the appendeddrawings. However, the appended drawings illustrate only typicalembodiments of the disclosure and are therefore not to be consideredlimiting of scope, for the disclosure may admit to other equallyeffective embodiments.

FIG. 1 is a schematic diagram of a system for forming a plurality ofnonvolatile memory cells in a 3D NAND memory device, in accordance withat least one embodiment of the present disclosure.

FIG. 2 is a flowchart of a method for forming a plurality of nonvolatilememory cells in a 3D NAND memory device, in accordance with at least oneembodiment of the present disclosure.

FIGS. 3A-3P are schematic cross-sectional views of a portion of a 3DNAND memory device, in accordance with at least one embodiment of thepresent disclosure.

FIGS. 4A-4C are schematic cross-sectional views of a portion of a 3DNAND memory device, in accordance with at least one embodiment of thepresent disclosure.

FIG. 5 is schematic cross-sectional views of a portion of a 3D NANDmemory device, in accordance with at least one embodiment of the presentdisclosure.

To facilitate understanding, identical reference numerals have beenused, where possible, to designate identical elements that are common tothe figures. The figures are not drawn to scale and may be simplifiedfor clarity. Elements and features of one embodiment may be beneficiallyincorporated in other embodiments without further recitation.

DETAILED DESCRIPTION

Embodiments described herein generally relate to 3D NAND memory deviceswith improved word-line isolation and methods of forming the same.Specifically, alternative layers of material, e.g., a first layer ofmetal and a second layer of metal which are different types of metals)multi-layers are used for 3D NAND cell film stack to form memory holes.One of the metal layers (e.g., the first metal can be subsequentlyremoved (e.g., etched) forming spaces that are then filled with one ormore materials, e.g., a low k oxide (e.g., SiO, SiO₂. etc.) or an airgap). Both metal layers can be etched out using the same etchchemistries. Thus, (high aspect ratio) HAR etch can be performed withhigher throughput. For example, both metals can be etched away using drychemical etching containing hydrofluoric acid (HF) with a highselectivity (e.g., >100:1). Moreover, embodiments described hereineliminate a wordline (WL) metal filling step, which is sometimes usedwith conventional methods for forming 3D NAND memory devices and whichis a critical step for replacement metal gate (RMG), e.g., used withoxygen nitrogen (ON) mold. As described herein, WL metal can bedeposited as mold stacks and silicon oxide can be filled after removingthe TiN; SiO₂ filling is a much easier and cost effective process thanconventional processes used for WL metal filling. Also, voids that cansometimes form due to incomplete filling of the SiO₂ is not harmful tothe fabricated 3D NAND memory devices described herein, as the voids canfunction as air gaps (which can be formed without incorporating anyextra-steps), as opposed to voids formed during conventional RMGprocesses, which can result in serious SiO₂ degradation due to remainingfluorine (F) gas that can be present in the voids. Furthermore,mechanical stress of mold stacks used in forming the 3D NAND memorydevice can be modulated by deposition conditions of metal using physicalvapor deposition (PVD) or chemical vapor deposition (CVD), and overallstack height can be thinner, when compared to current SiO₂/silicon(Si₃N₄) multi-layers, e.g., as a result of not having to use RMG.

FIG. 1 is a schematic diagram of a system 100 for forming a plurality ofnonvolatile memory cells in a 3D NAND memory device (e.g., memory device300 of FIGS. 3A-3P). FIG. 2 is a flowchart of a method 200 for formingthe plurality of nonvolatile memory cells in the memory device,according to an embodiment of the present disclosure. FIGS. 3A-3P areschematic cross-sectional views of a portion of a 3D NAND memory deviceduring stages of fabrication in accordance with at least one embodimentof the present disclosure, for example, using the method 200.

FIG. 3A shows the memory device 300, which can be a Bit Cost Scalable(BiCS) device, including a string (plurality) of vertically stackedmemory cell layers 302 (e.g., a conductive layer used as word line(e.g., a second layer of material) alternately disposed between aplurality of layers 304 (e.g., a first layer of material), formed on asubstrate 301, which in some embodiments can be a semiconductor.

The substrate 301 can be any suitable starting material for formingintegrated circuits, such as a silicon (Si) wafer or a germanium (Ge)wafer. The semiconductor substrate 301 may be a silicon semiconductorsubstrate having a layer or layers formed thereon, such as a film stack,employed to form a structure on substrate 301, such as the memory device300. The substrate 301 may include a material such as crystallinesilicon (e.g., Si<100> or Si<111>), Si3N4, strained silicon, silicongermanium, doped or undoped poly-silicon (poly-Si), doped or undopedsilicon, patterned or non-patterned wafer, silicon on insulator (SOI),carbon-doped silicon oxides, silicon nitride (SiN, Si₃N₄, etc.), dopedsilicon, germanium, gallium arsenide, glass, sapphire, metal layersdisposed on silicon, and the like. The substrate 301 may be a roundwafer, such as a 200 mm, 300 mm, or 450 mm diameter wafer, or as arectangular or square panel.

In some embodiments, the memory cell layers 302 and layers 304 can beformed on a common source line (CSL) layer, which can be formed on anetch stop layer (ESL). In such embodiments, the CSL layer and the ESLcan be made from materials such as tungsten (W), silicon nitride (SiN),poly-Si, or combinations thereof. In some embodiments, a mask layer (ML)(e.g., a silicon oxide layer) can be deposited atop the memory celllayers 302 or the layers 304 to form a top or final layer of material.The ML is patterned before etching stacks to cover area which is not tobe removed during stack etching process.

Layers 304 are disposed between memory cell layers 302. The layers 304may be formed using any suitable material (e.g., metal, metal nitride,or a conductive metal compound) such as W, molybdenum (Mo), tantalum(Ta), niobium (Nb), osmium (Os), zirconium (Zr), iridium (Ir), rhenium(Re), titanium (Ti), Ti nitride (N), TaN, WN, MoN, ZrN, WO_(x), RuO_(x),IrO_(x), etc. The layers 304 are provided to facilitate forming (orbuilding) the memory cell layers 302 on the semiconductor substrate 301.After the memory cell layers 302 are formed, the layers 304 are removedusing one or more suitable processes and filled with one or moresuitable materials, as will be described in greater detail below.

Each of the memory cell layers 302 corresponds to a word line of thememory device 300, each word line extending into the page to formadditional memory cells of the memory device 300 that are not visible.Thus, each of the memory cell layers 302 is configured to store one ormore bits of data. As such, each of the memory cell layers 302 can beformed using any suitable material (e.g., metal, metal alloy, metal withdopant including one or more metal elements) such as W, tungstensilicide (WSi), tungsten poly-Si (W/poly-Si), tungsten alloy, Ta, Ti,Nb, Os, Zr, Ir, Re, copper (Cu), ruthenium (Ru), nickel (Ni), cobalt(Co), chromium (Cr), iron (Fe), manganese (Mn), aluminum (Al), hafnium(Hf), vanadium (V), molybdenum (Mo), palladium (Pd), gold (Au), silver(Au), platinum (Pt), alloys thereof, nitride compounds thereof, such astitanium nitride (TiN) and tantalum nitride (TaN), and combinationsthereof, among others. For each substrate 301, the memory cell layers302 and the layers 304 are be formed from different materials. Forexample, in at least some embodiments, the memory cell layers 302 can beformed from W while the layers 304 can be formed from TiN; othermaterial combinations can also be used.

Continuing with reference to FIG. 3A, at 202, the memory cell layers 302and layers 304 can be deposited on the semiconductor substrate 301 usingany suitable deposition processes and/or apparatus 130 (FIG. 1 ),examples of which can include a chemical vapor deposition (CVD)apparatus 130 a, a physical vapor deposition (PVD) apparatus 130 b, oran atomic layer deposition (ALD) apparatus 130 c. For example, in oneparticular embodiment, the layers 304 (e.g., TiN) can be depositedusing, for example, the PVD apparatus 130 b, which can be a stand-aloneapparatus or a part of a cluster tool, that is configured, for example,to perform a PVD process. Exemplary apparatus that can be configured forperforming the above process can include, for example, the ENDURA®VERSA® line of stand-alone PVD apparatus, available from AppliedMaterials, Inc. Similarly, the memory cell layers 302 (e.g., W) can bedeposited using for example, the CVD apparatus 130 a, which can be astand-alone apparatus or a cluster tool, that is configured, forexample, to perform a CVD process. Exemplary apparatus that can beconfigured for performing the above process can include, for example,the PRODUCER® APF line of stand-alone CVD apparatus, available fromApplied Materials, Inc. Alternatively or additionally, the layers 304can be deposited using, for example, the CVD apparatus 130 a, and thememory cell layers 302 can be deposited using for example, the PVDapparatus 130 b,

Next, the WL staircase can be formed by etching the memory cell layers302, the layers 304, and the ML (FIG. 3B). For example, any suitableetching apparatus 110 (FIG. 1 ) and/or method may be employed to formthe WL staircase such as deep reactive-ion etching (DRIE), a highlyanisotropic etch process employed to create high aspect-ratio holes andtrenches in wafers or other substrates. Etching gases suitable for suchetching processes can include fluoride (SF₆, CF₄, CHF₄, CH₃F, C₂F₆,C₄F₈, and NF₃), chloride (HCl, C₂, BCl₃), bromide (Br₂, HBr), or, anoxygen containing gas (e.g., O₃, O₂, CO₂, CO, H₂O, NO, NO₂, N₂O, CO, andthe like) and optionally may include an inert gas, such as argon (Ar) orhelium (He).

After the WL staircase has been formed, an interlayer dielectricdeposition (ILD) process can be performed to deposit a layer of material305 over the memory cell layers 302 and the layers 304. The ILD processcan use dielectric materials to that are to be filled in an area wherethe staircase is formed. In at least some embodiments, a thick siliconoxide (around ˜1.2 times thicker than the stack height of the memorycell layers 302 and layers 304) is deposited and planarized by chemicalmechanical polishing (CMP)

Next, with reference to FIG. 3C, using the etching apparatus 110 atleast one memory hole 306 (or memory holes 306, e.g., three memory holes306) are formed in the ML, the stack of alternating memory cell layers302 and layers 304, the CSL, and partially in the ESL. Alternatively oradditionally, the memory holes 306 can be formed to extend into thesubstrate 301. The string of vertically stacked memory cell layers 302and layers 304 are shown arranged with four vertical columns. Theetching apparatus 110 can be configured to use sulfur hexafluoride (SF6)chemistries with ion acceleration voltage ranging from 0.5˜10 kV. A hardmask deposition process may first be performed prior to performing theetching, and a hard mask layer that is deposited prior to etching can beremoved after etching is complete and the memory hole 306 is formed.Other etching apparatus and/or processes can be used to form the memoryholes 306.

With reference to FIGS. 3D and 3E, after the memory holes 306 areformed, one or more additional layers of material can be deposited inthe memory holes 306. For example, as shown in the indicated area ofdetail of FIG. 3E, a layer (e.g., a continuous layer) of aluminum oxide(AlO) (layer 307) is first deposited on sides that define the memoryholes 306 and along the ESL at the bottom of the memory holes 306. Next,a layer of silicon oxide (layer 309) is deposited atop the layer A andalong the bottom of the memory holes 306. Next a layer of trap-siliconnitride (SiN) (layer 311) is deposited atop the layer 309 and along thebottom of the memory holes 306. Next, another layer of silicon oxide 313is deposited atop the layer 311 and along the bottom of the memory holes306. Next, a layer of poly-Si (layer 315) is deposited atop the layer ofsilicon oxide 313 and along the bottom of the memory holes 306 to form apoly-Si channel at the bottom of the memory hole 306. Next, a coresilicon oxide (layer 317), e.g., SiO, SiOC, etc., is deposited to fillthe poly-Si channel (see FIG. 3E, for example). The layers 307-317 canbe deposited using any suitable deposition processes and/or apparatus.For example, the CVD apparatus 130 a and the PVD apparatus 130 b of FIG.1 can be used to perform CVD and PVD, respectively, to deposit thelayers 307-317. Alternatively or additionally, the ALD apparatus 130 c,which can be a stand-alone apparatus or a cluster tool, that can be usedto perform an ALD process to deposit the layers 307-317. Exemplaryapparatus that can be configured for performing the above processinclude, for example, the OLYMPIA line of ALD apparatus, available fromApplied Materials, Inc.

After the layer 317 is deposited to fill the poly-Si channel, anadditional layer 321 (e.g., a layer of poly-Si) can be deposited atopthe layer 317 to cover the layer 317 and an additional ML layer may bedeposited atop the layer 321 to cover the layer 321, as shown in FIGS.3F and 3G.

Next, with respect to FIG. 3H, two additional slits or holes 308 can beformed (e.g., using the above-described etching process) in the ML, thestack of alternating memory cell layers 302 and layers 304, the CSL, theESL, and partially into the substrate 301. Unlike the memory holes 306,however, the holes 308 are used to remove the CSL and the layer 304. Forexample, after the holes 308 are formed, the CSL is removed using theabove-described etching process (e.g., wet etch and/or chemical dryetch) and so are the layers 309-313 that were deposited in the memoryholes 306 within the CSL (see FIGS. 3I and 3J, for example).

Next, the areas that included the CSL and the layers 307-313 are filledwith a phosphorous doped poly-Si (n+ type silicon) layer (e.g., a layer323) and the holes 308 are left intact, e.g., not filled or minimallyfilled with the layer 323 (FIG. 3K).

Next, at 204, the layers 304 are removed using the above above-describedetching process (e.g., wet etch or chemical dry etch using the etchingapparatus 110). More particularly, the layers 304 (e.g., layers of TiN)are removed by selectively oxidizing the layers 304 to form spaces 325between alternating layers of the memory cell layers 302 (e.g., layersof W), as depicted in FIG. 3L.

Removal of the layers 304 may be achieved using any suitable etching orpatterning processes to selectively remove the layers 304 of from thememory device 300 without undesirably damaging the memory cell layers302.

For example, any isotropic etch process that is selective to at leastthe memory cell layers 302 may be employed to remove the layers 304 withhigh selectivity. For example, in some embodiments, the layers 304 canbe removed with a reactive species that is formed via a remote plasmafrom a process gas comprising oxygen (O₂) and nitrogen trifluoride(NF₃), such as an etching apparatus 120 of FIG. 1 . The isotropic etchprocess can be performed in any suitable isotropic etch apparatus.Highly selective, isotropic dry etching processes that may be used forthe removal of the layers 304 are described in U.S. Pat. No. 9,165,786,entitled “Integrated oxide and nitride recess for better channel contactin 3D architectures” and filed Aug. 5, 2014. The dry etch process may beperformed using a suitable dry etching apparatus. Exemplary apparatusthat can be configured for performing the above process include, forexample, the PRODUCER® SELECTRA® line of etching apparatus (FIG. 1 ),available from Applied Materials, Inc., of Santa Clara, Calif.

Alternatively or additionally, to remove the layers 304 a selectiveoxidation apparatus 140 can be used to deposit a silicon oxide layer(not shown) on the layers 304 using rapid thermal oxidation (RTO),radical oxidation, or remote plasma oxidation (RPO), for example,decoupled plasma oxidation (DPO). In some embodiments, where a lowthermal budget and/or reduced diffusion of oxygen are desired, plasmaoxidation or radical oxidation may be utilized. As used herein, a lowthermal budget means a thermal budget less than a furnace process oftens of minutes at 850 degrees Celsius peak temperature. For example,when RPO is used at 204, one or more suitable plasma reactors, such asRPO reactors available from Applied Materials, Inc. can be used toprovide the silicon oxide layer on the layers 304.

Alternatively, a high thermal budget processes (i.e., high oxygendiffusion) may also be utilized. For example, high thermal budgetprocesses (e.g., wet, dry, or RTO) can provide conformal oxidation,faster oxidation rates, and thicker oxidation.

The type of selective oxidation apparatus 140 and/or etching apparatus120 used to remove the layers 304 of carbon can depend on one or morefactors including, but not limited to, time constraints, desiredoxidation rates, etc.

Regardless of the selective oxidation apparatus 140 and/or etchapparatus 120 (or etch process using the etch apparatus 110) used, afterremoval of the layers 304 from the memory device 300, a suspended filmstack with only the memory cell layers 302 remains on the substrate 301for further processing, see FIG. 3L.

In some embodiments, at 206, with reference to FIG. 3M, a layer ofmaterial 327 (e.g., low k (dielectric constant) oxide material, siliconoxide, silicon dioxide, etc.) can be deposited to fill the spaces 325(e.g., with no air gaps). The layer of material 327 can be depositedusing, for example, the CVD apparatus 130 a or the ALD apparatus 130 cof FIG. 1 . The low k oxide material can include, but is not limited to,silicon oxide, silicon dioxide, etc. The layer of material 327 can havea dielectric constant of 3.9 and smaller than 3.9.

Conversely, with reference to FIG. 3N, at 204 in some embodiments, thelayer of material 327 can be deposited to partially fill the spaces 325to leave air gaps 329 therein. The layer of material 327 can bedeposited using, for example, the CVD apparatus 130 a or the ALDapparatus 130 c of FIG. 1 . The spaces 325 can be partially filled suchthat the air gaps 329 can take up any specific volume of the spaces 325.

After one of the processes of 206 are completed, the memory device 300will have the stack of alternating memory cell layers 302 and the layerof material 327 (e.g., low k oxide material) with the air gaps (FIG. 3N)or without the air gap 329 contained therein (FIG. 3M). Once formed, the3D NAND memory device 300 can be further processed to deposit a gatesilicon oxide, e.g., for gate formation.

For example, after the processes of 206 are completed, the holes 308 canbe filled (e.g., planarization) with one or more suitable materialsincluding, but not limited to, TiN, W, SiN, oxide, or combinationsthereof (FIG. 3O). Similarly, after planarization has been performed,one or more back end of the line (BEOL) processes (e.g., WL staircontact formation) can be performed to complete fabrication of the 3DNAND memory device 300 (FIG. 3P).

FIGS. 4A-4C are schematic cross-sectional views of a portion of 3D NANDmemory devices 400 a-400 c, in accordance with at least one embodimentof the present disclosure. The 3D NAND memory devices 400 a-400 c aresubstantially similar to the 3D NAND memory device 300. Accordingly,only those features that are unique to the 3D NAND memory devices 400a-400 c are herein described.

As illustrated in FIG. 4A, prior to 206 (e.g., depositing a layer ofmaterial (e.g., a layer of material 427 b and 427 c to fill spaces 425 a(e.g., with or without air gaps 429 c, as described above)), one or morelayers of the layers that fill the memory holes (e.g., layers 407 b-415b or layers 407 c-415 c) can be removed from the memory cell layers402).

For example, as shown in the indicated area of detail in FIG. 4B,instead of applying a continuous layer 407 b of the AlO, a discontinuouslayer 407 b may be formed to only cover the memory cell layers 402 b(and not the layers 404 b) on sides that define the memory holes andalong the ESL at the bottom of the memory holes. The memory cell layers402 b having a discontinuous layer 407 b can be made by removing thelayer of 407 b from the area in the memory hole adjacent to where thelayer of material 427 b is to be deposited prior to 206. By using thediscontinuous layer 407 b, cell-to-cell interference between theneighboring memory cell layers 402 can be reduced. For illustrativepurposes, the 3D NAND memory device 400 b is shown without air gaps.

Similarly, a discontinuous layer 407 c and discontinuous layers ofsilicon oxide and SiN (e.g., layers 409 c and 411 c) can be used to formthe 3D NAND memory device 400 c (FIG. 4C). The memory cell layers 402 chaving discontinuous layers 407 c-411 c can be made by removing thelayers 407 c-411 c from the area in the memory hole adjacent to wherethe layer of material 427 c is to be deposited prior to 206. The memorycell layers 402 c having discontinuous layers 407 c-411 c can preventdata loss through the layer 411 c (e.g., trap SiN) between theneighboring memory cell layers 402 c. For illustrative purposes, the 3DNAND memory device 400 is shown with air gaps 429 c.

FIG. 5 is schematic cross-sectional view of a portion of a 3D NANDmemory device 500, in accordance with at least one embodiment of thepresent disclosure. The inventors have found that the present disclosureis not limited to charge trap based NAND flash memory devices. Forexample, a memory cell with a resistive RAM (ReRAM) or phase changememory (PCM) can be formed using the methods described herein. Moreparticularly, as illustrated in FIG. 5 , a resistive layer 550 ofresistive memory material (e.g., Ta₂O₅, TiO₂, etc. for ReRAm orGe_(x)Sb_(y)Te_(z) (GST), etc., for PCM) can be deposited between thememory cell layers 502 and the layer 515, which can be made from thesame material as the layer 515 (e.g., for forming a poly-Si channel.

The methods described herein can be used to form the 3D NAND memorydevice, and cross-talk, e.g., leakage of trapped charges, amongneighboring memory cells of the memory cell layers 302 of the memorydevice 300 is reduced, if not eliminated, by forming the plurality ofmemory cells layers 302 with the layers 304, which can be removed andreplaced with the material 327 (e.g., low k oxide material, siliconoxide, etc.) with or without the air gap 329 contained therein.Moreover, since both the memory cell layers 302 and layers 304 can beetched out using oxygen based etch processes, high aspect ratio memoryhole etch and gap fill can be less challenging when compared toconventional processes. Furthermore, when the memory cell layers 302 andthe layers 304 are formed from one or more of the aforementionedmaterials, mechanical stress of the mold stacks can be modulated by thedeposition conditions of the aforementioned materials, which, in turn,can reduce, if not eliminate, the likelihood of pattern collapse, andcan allow for the overall stack height of the memory device 300/400 tobe relatively thin when compared to conventional memory devices.Additionally, the use of conventional replacement metal gate processes,which are sometimes used to build word line staircase, are eliminated,as the memory cell layers 302 are made from one or more of the abovedescribed metals (e.g., W).

While the foregoing is directed to embodiments of the presentdisclosure, other and further embodiments of the disclosure may bedevised without departing from the basic scope thereof.

The invention claimed is:
 1. A method for forming a plurality ofnonvolatile memory cells, comprising: forming, on a substrate, a stackof alternating layers of a first layer of metal and a second layer ofmetal different from the first layer of metal; forming at least onememory hole in the stack of alternating layers of the first layer ofmetal and the second layer of metal; depositing in the at least onememory hole: a layer of silicon nitride (SiN) atop a first layer ofsilicon oxide (SiO); a second layer of SiO atop the layer of SiN; alayer of poly-silicon (poly-Si) atop the second layer of SiO to form apoly-Si channel; and a core silicon oxide to fill the poly-Si channel;removing the first layer of metal to form spaces between alternatinglayers of the second layer of metal; and one of depositing a first layerof material to partially fill the spaces to leave air gaps therein ordepositing a second layer of material to fill the spaces.
 2. The methodof claim 1, wherein depositing the first layer of material to partiallyfill the spaces to leave air gaps therein or depositing the second layerof material in the spaces is performed using one of chemical vapordeposition or atomic layer deposition.
 3. The method of claim 1, whereinthe first layer of metal and the second layer of metal are depositedusing at least one of chemical vapor deposition and physical vapordeposition.
 4. The method of claim 1, wherein removing the first layerof metal is performed using one of: a dry chemical etch processcontaining F chemistries comprising fluorine compounds including atleast one of SF₆, CF₄, CHF₄, CH₃F, C₂F₆, C₄F₈, or NF3; or a wet etchprocess.
 5. The method of claim 1, wherein the substrate comprises acommon source layer.
 6. The method of claim 5, wherein the common sourcelayer comprises at least one of tungsten, SiN, or poly-Si.
 7. The methodof claim 1, further comprising depositing a layer of aluminum oxide(AlO) in the at least one memory hole.
 8. The method of claim 7, furthercomprising depositing the first layer SiO atop the layer of AlO.
 9. Themethod of claim 8, wherein forming the at least one memory hole isperformed using a dry chemical etch process containing F chemistriescomprising fluorine compounds including at least one of SF₆, CF₄, CHF₄,CH₃F, C₂F₆, C₄F₈, or NF₃.
 10. The method of claim 9, further comprising,prior to removing the first layer of metal to form spaces between thealternating layers of the second layer of metal: forming at least twoslits through the first layer of metal, the second layer of metal, andthe layer of SiN and poly-Si using F-based chemistry comprising fluorinecompounds including at least one of SF₆, CF₄, CHF₄, CH₃F, C₂F₆, C₄F₈, orNF₃; removing the layer of SiN and poly-Si from the substrate using oneof a wet etch process or a chemical dry etch process; removing, from theat least one memory hole in an area that was occupied by the layer ofSiN and poly-Si prior to removal thereof, the layer of AlO, the firstlayer of silicon oxide atop the layer of AlO, the layer of SiN atop thefirst layer of silicon oxide, and the second layer of SiO atop the layerof SiN using the chemical dry etch process; and depositing a layer ofphosphorous doped poly-Si on the substrate in place of a removed layerof AlO, a removed first layer of silicon oxide, a removed layer of SiN,and a removed second layer of silicon oxide to cover a portion of thepoly-Si channel.
 11. The method of claim 10, further comprising,subsequent to removing the first layer of metal to form spaces betweenthe alternating layers of the second layer of metal and prior to one ofdepositing the first layer of material to partially fill the spaces toleave air gaps therein or depositing the second layer of material tofill the spaces: removing, from the at least one memory hole in an areathat was occupied by the layer of first metal prior to removal thereof,the layer of AlO, the first layer of silicon oxide atop the layer ofAlO, and the layer of SiN atop the first layer of silicon oxide usingthe chemical dry etch process.
 12. The method of claim 1, wherein thefirst layer of metal is at least one of tungsten (W), molybdenum (Mo),tantalum (Ta), niobium (Nb), osmium (Os), zirconium (Zr), iridium (Ir),rhenium (Re), titanium (Ti), Ti nitride (TiN), TaN, WN, MoN, ZrN, WOx,RuOx, and IrOx, wherein the second layer of metal is one of W, Mo, Ta,Ru, Nb, Os, Zr, Ir, Re, and Ti, wherein the first layer of material issilicon oxide, and wherein the second layer of material is a low koxide.
 13. The method of claim 12, wherein the low k oxide is one ofsilicon oxide or silicon dioxide having a dielectric constant that isless than or equal to 3.9.